| Abstract
| - In this article, the microstructural properties of the phases which form in samples of some aluminium-based alloys, have been investigated. The study was focussed on the characteristic parameters of the formed phases in the ternary Al(rich)-Cu-Zn alloys by means of X-ray diffraction (XRD) analysis and optical microscopy observations. The bulk materials of ternary Al-X wt.%Cu-X wt.%Zn (X = 2, 8, 20, 25) alloys have been made under vacuum by the high frequency (HF) magnetic induction melting process and rapidly solidified at ambient temperature from compacted composite targets of a mixture of high purity (99.99%) of Al , Cu and Zn laboratory powders. Results are correlated with that of binary Al-Cu alloys.
- Dans cet article, les propriétés microstructurales des phases, qui se développent dans des échantillons de quelques alliages à base d’aluminium, ont été étudiées. L’étude a été focalisée sur les paramètres caractéristiques des phases formées dans les alliages ternaires Al(riche)-Cu-Zn par l’intermédiaire des analyses de diffraction de rayons X (DRX) et observations de microscopie optique. Les matériaux massifs des alliages ternaires Al-X m.%Cu-X m.%Zn (X = 2, 8, 20, 25) ont été élaborés sous vide par la procédé de fusion à induction magnétique haute fréquence (HF) et solidifies rapidement à la temperature ambiante à partir de cibles composites compactées d’un mélange poudres Al, Cu et Zn de grande pureté de laboratoire (99,99 %). Les résultats sont corrélés avec celles des alliages binaires Al-Cu.
|